EPUSELF 161L
Article No. 000175
EPUSELF 161L – is a three component backfill mass based on an epoxy resin, including a more special filler combination. With the hardener EPH 7525.
Application
To obtain high modulus back-filled tools by the combination of wear-resistant surface resins and supporting structures made of steel.
Particularly suitable for foaming tools, blowing tools, plate working tools, rolls, spindles or the like.
Properties
- Highest strength
- No crack initiation due to a low exothermic reaction
- Thermal expansion coefficient adjusted on steel
- Possibility of “Do-it-yourself”-casting
List prices for purchase quantities of:
Quantity | Price per kg in € plus VAT |
0 - 500 kg | 10,30 |
501 kg - 1.000 kg | 10,00 |
1.001 kg - 3.000 kg | 9,90 |
Density | approx. 2,5 g/cm³ |
Compressive strength1 | > 120 MPa |
Flexural strength1 | > 35 MPa |
Modulus of elasticity | > 36,0 GPa (dynamic2) > 35,0 GPa (static1) |
Thermal expansion coefficient | approx. 10 * 10-6 K-1 at 20 °C |
Thermal conductivity | approx. 4,8 W/m K at 25 °C |
Specific heat capacity | approx. 1,0 J/g K at 25 °C |
Thermal diffusivity | approx. 1,8 mm 2/s at 25 °C |
Deflection temperature | ca. 100°C (after post-curing) |
Logarithmic decrement | 0,03 |
Wall thickness of cast | 15 - 300 mm |
Maximum grain size | 3 mm |
Mixing ratio | A : B : C = 1,9 : 0,75 : 22,35 (parts by weight) |
Pot life | approx. 4 - 5 hours at 23°C |
Processing temperature | 15 – 25 °C |
Curing Time | approx. 24 hours |
Brochure Do-it-yourself mineral casting EPUSELF
The high-performance mineral casting system for do-it-yourself filling and casting of vibration-damping ...
Brochure
Download PDF (1 MB)English
EPUMENT 161 L / EPH 7525 - Technical Data Sheet
Product Information / Data Sheet
Download PDF (46 KB)English
Broschüre Mineralguss zum Selbermachen EPUSELF
Das leistungsfähige Mineralguss-System zum Selbstverfüllen und -vergießen von schwingungsdämpfenden Bauteilen ...
Brochure
Download PDF (1 MB)German